Table 2.
The physical and mechanical properties of ceramics made at different carbonization temperature

Impregnation rate (%)	Temperature(℃)	Density(kg/㎥)	MOR(MPa)	MOE(GPa)	Brinell hardness(MPa)	Compression strength(MPa)
30	800	558.57(30.63)	2.76(0.83)	1.21(0.31)	5.11(0.85)	3.44(1.18)
40	800	617.08(49.90)	3.25(0.75)	1.63(0.34)	7.15(1.58)	5.09(1.35)
50	800	627.10(29.84)	3.30(0.97)	1.66(0.39)	6.85(1.72)	6.73(2.11)
60	800	649.10(30.15)	3.74(0.95)	1.82(0.41)	7.55(2.39)	9.65(2.35)
Parenthesis is standard deviation; MOE: modulus of elasticity; MOR: modulus of rupture; Mean value from 10 replications;